摘要：本文依据温拌沥青的主要作用机理，采用益路

™DAT（Evotherm）温拌沥青技

术，充分考虑施工和易性及降温规律进行温拌沥青混合料施工时效研究。试验结果表明，益
路温拌剂不改变沥青粘度，沥青粘度随温度下降呈指数关系增加，且温拌沥青混合料与环
境温度相差较少，据此对延长冬季沥青路面施工提出了温控建议。

 

　　关键词：温拌沥青混合料

 施工时效 

　　

Abstract: based on the main function of temperature mix asphalt mechanism, the profit road 

™  DAT  (Evotherm)  temperature  mix  asphalt  technology,  full  consideration  construction 
workability  and  cooling  rule  temperature  mix  asphalt  mixture  construction  aging  research.  The 
test  results  show that the temperature: road asphalt mixing agent don't change viscosity,  asphalt 
viscosity  with  temperature  drop  increase  exponentially  with  relationship,  and  temperature  mix 
asphalt  mixture  and  environmental  temperature  varies  less,  then  extend  winter  construction  of 
asphalt pavement temperature control Suggestions put forward. 
　　

Key words: wen mix asphalt mixture construction time 

　　

 

　　

 

　　中图分类号：

U416.217 文献标识码：A 文章编号： 

　　

 基于表面活性剂平台的温拌沥青混合料（WMA）路面技术是国际上近几年研发并逐

步推广应用的新技术。与传统热拌沥青混合料相比，在不改变材料配比和施工工艺以及温拌
沥青混合料性能不低于热拌沥青混合料的前提下，混合料拌和与碾压温度降低

30

℃～

40

℃。温拌技术可节省燃油 20%-30%，减少温室气体排放 60%左右，减少沥青烟等有毒气

体排放

80%以上，伴随施工温度的降低，同时减少了沥青在施工过程的老化、提高沥青混合

料路用性能，延长使用寿命、减少道路的寿命周期养护费用，是名符其实的高节能、低排放
的高新技术。

 

　　

 本文采用益路温拌沥青技术，根据温拌混凝土的施工时效研究结果，给出了正常温度

环境下和低温条件下温拌混凝土的温度控制建议，对延长冬季沥青路面施工建设期，提高
路面施工质量，减低施工环境污染具有一定的参考价值。

 

　　一

 、原材料及实验方法 

　　

 1.1 原材料 

　　

 （1）粗集料：采用石灰岩碎石，洗净，烘干后，筛分成每一档备用，确保级配准确。 

　　

 （2）细集料采用石灰岩石屑，洗净烘干后，筛分成每一档备用。 

　　

 （3）填料：采用石灰岩矿粉， 

　　

 （4）沥青：采用佛山高富 AH-70 沥青及壳牌鄂州 SBS 改性沥青，两种沥青均为长沙

市沥青混合料拌合站常用的沥青。其指标如下表

1，符合规范要求。 

　　

 表 1AH-70 沥青三大指标 

　　

 

　　

 

　　

 

　　表

2SBS 改性沥青三大指标 

　　

 

　　

 

　　

 

　　

 （5）温拌剂：美德维实伟克公司的益路牌（Evotherm）温拌剂 DAT-H5（10F）。 

　　

1.2 试验方法