摘要：本文结合实验室和工业试验的数据，讨论了转炉炼钢用石灰石代替石灰造渣过程中石灰石的行

为，结果认为，转炉炼钢前期直接加入石灰石做造渣原料，可以很快完成煅烧化渣过程，并且在某些方

面比使用石灰有利；用石灰石造渣能够达到希望的结果，石灰石分解大概在 5～6 分钟内完成；高温有

利于碳酸钙的快速分解，1400℃与 1100℃相比，虽然温度只差 300℃，分解率大 3～4 倍，因此分解化

渣与前期温度密切相关。

关键字：

  

  

  

   

转炉炼钢 石灰石 分解 造渣 温度

Primary research on the behavior of limestone charged into 

converter during making slag process

LI Zi-quan，LI hong，GUO Luo-fang，YAN Peng-cheng

(School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 

100083, China)

DONG Da-xi，LIANG Zi，WANG Gong-liang，ZHANG Hong-wei，LI Sheng-li

(Shijiazhuang Iron Steel Co．，Ltd．，Shijiazhuang 050031，Hebei，China)

Abstract：The behavior of limestone which is utilized for slagging instead of lime during converter steelmaking 

process was discussed with the data collected from laboratorial and industrial. The result can be concluded that: 

limestone which is directly charged into converter as slag-forming material during early period of steelmaking 

process can be quickly decomposed and participate in making slag, in addition, it has more advantages over lime 

in several respects; the anticipant result can be got using limestone to make slag, and limestone is completely 

decomposed during 5~6 minutes  in converter  steelmaking  process;  high temperature is propitious  to calcium 

carbonate decomposing, just as the result of laboratory experiments shows that the decomposition rate of CaCO

3

 at 

1400  is 3~4 times greater than that at 1100  in spite of only 300

 difference, therefore, the early period

℃

℃

℃

 

temperature has a great effect on the decomposition and slagging processes. 

Key words: steelmaking in BOF   limestone   decomposing   slag making   temperature

北京科技大学提出了一种新的炼钢方法

[1]

，用石灰石代替石灰加入转炉造渣炼钢，已

在国内两个钢铁公司进行工业试验取得了成功，这一方法是对氧气转炉炼钢工艺的大变

革，在低碳炼钢节能减排方面具有重要的意义

[2,3]

。石灰石在开吹后加入转炉，在铁水面上

立刻开始煅烧化渣过程，与现行生产工艺石灰入炉后的行为有很大的差异，因此有必要

对这一过程进行深入的研究讨论。

1 研究方法

1