Corrosion Behavior of Zn/Al Based Sacrificial Anode Coatings in

Simulated

Low-temperature Sea Environment

Abstract

In the field of seawater corrosion protection, more and more start using thermal spraying metal

coating or sacrificial anode protection system. But relatively harsh in deep sea corrosion environment, the

lack of experience and relevant theory make people in the corrosion protection measures when the lack of

sufficient theoretical support, and deep in the construction, testing, maintenance is not easy to realize and

high cost, this requires a deep need to be more reliable guarantee. So they asked us to reduce the cost as

much as possible to improve the reliability of cathodic protection at the same time. That is how to

guarantee the anti-corrosion requirements, reduce the weight of the sacrificial anode blocks or use

appropriate way reasonable alternative sacrificial anode has important engineering significance.

This paper tries to use aluminum instead of aluminum sacrificial anode coating in order to reduce the

dosage of anode. Through laboratory accelerated simulated Marine corrosion test at low temperature, to

study the corrosion resistance and the corrosion behavior is analyzed and discussed, and the aluminum

coating under different conditions of cathodic protection of the corrosion rate was studied, and try to

evaluate its life.

Studies have shown that under all kinds of atmosphere, the aluminum alloy anode coating protective

effect is better; Under the saturation of oxygen, aluminum coating has good corrosion protection effect.

Alternative ways are higher than the life of a piece of the life of the sacrificial anode and the anode block

+ coating protective way more to prolong the life of both sides.

Through observation of the specimen corrosion morphology, which can be found that, under the

saturation of oxygen, aluminum sacrificial anode polarization short time at the beginning of the cathodic

protection, corrosion current is bigger, life is short; Aluminum coating the surface passivation

continuously, life is long; In anode + coating, corrosion current smaller, easier to passivation coating,

further extend the service life.

Key words:

sacrificial anode

, coating , arc spraying,

corrosion and protection